Utjecaj nanočestica cerijevog (IV)-oksida na postojanost sustava drvo-premaz pri izlaganju vanjskim utjecajima

diplomski rad

• Naslov (engleski): The impact of cerium dioxide nanoparticles on wood-coating system during weathering
• Autor: Jure Beljo
• Mentor: Vlatka Jirouš Rajković (mentor)
• Član povjerenstva: Vlatka Jirouš Rajković (predsjednik povjerenstva)
• Član povjerenstva: Hrvoje Turkulin (član povjerenstva)
• Član povjerenstva: Josip Miklečić (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Šumarski fakultet; (Zavod za namještaj i drvne proizvode); Zagreb
• Datum i država obrane: 2016-09-29, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: BIOTEHNIČKE ZNANOSTI; Drvna tehnologija; Konstruiranje i oblikovanje proizvoda od drva

Sažetak

U ovom je istraživanju ispitivana postojanost drva površinski obrađenog vodenom poliakrilatnom lazurom u koju su dodane nanočestice cerijevog (IV)-oksida pri ubrzanom laboratorijskom izlaganju. U istraživanju su korišteni nemodificirani i toplinski modificirani uzorci jasenovine. Nanočestice cerijevog oksida dodavane su u osnovni premaz u 3 različite koncentracije. Površinski obrađeni i neobrađeni (kontrolni) uzorci ubrzano su izlagani 6 tjedana u QUV uređaju opremljenom s UVA-340 lampama.Tijekom izlaganja na uzorcima je mjerena promjena boje i sjaja. Također je mjerena vodopropusnost sustava drvo-premaz potapanjem uzoraka. Rezultati istraživanja pokazuju da dodavanje nanočestica pozitivno utječe na postojanost toplinski modificiranih uzoraka, dok se za nemodificirane uzorake takav zaključak ne može donijeti. Nanočestice negativno utječu na sjaj uzoraka tijekom ispitivanja, dok utjecaja na vodoupojnost nema

Sažetak (engleski)

The durability of wood surface treated with water based acrylate varnish in which the nanoparticles of cerium (IV) oxide were added was researched during an accelerated laboratory exposure. Unmodified and thermally modified ash samples were used in this studiy. The nanoparticles of cerium oxide were added to the coating in 3 different concentrations. The coated and uncoated (control) samples were exposed for 6 weeks in the QUV device equipped with UVA-340 lamps. Color and gloss of the samples were measured during exposure. The permeability of wood-coating system was also measured by immersing samples in water. Results show that the addition of nanoparticles has a positive effect on the photostability of thermally modified samples, while for the non-modified samples such a conclusion cannot be made. Nanoparticles have a negative impact on gloss and no impact on water absorption.

• Ključne riječi: Nanopremaz; nanotehnologija; poliakrilatna lazura; QUV uređaj; boja; sjaj; cerijev oksid; vodopropusnost; jasenovina
• Ključne riječi (engleski): Nanotechnology; polyacrylate stain; QUV-conditioning; color; gloss; cerium oxide; water permeability; ash; nanoparticles
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:108:272914
• Studijski program: Naziv: Drvnotehnološki procesi; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra inženjer/inženjerka drvne tehnologije (mag.ing.techn.lign.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2016-11-21 10:22:10